Mold Finish – SPI Standard and the practical approach
SPI is the short form of the Society of Plastic Industry, who establish standards for plastic industry and the SPI Plastic Engineering Handbooks is one of the most important reference for engineers.
SPI defines the polishing standard on mold finish and widely applied in US markets. It helps to avoid grey areas and measure the finest of surface in the unit of Rough Average (Ra).
Nowadays, China’s standard is very much in line with SPI. However, there is little help using Ra value in China mold making industry because there is little chance to have precise equipment at site to do the precision measurement. What we needed is a practical guideline to more or less achieve the desired mold finish. Below guideline is widely accepted.
GLOSSY SURFACE, DIAMOND BUFF POLISH
SPI Finish A-1 — Grade #3, 6000 Grit Diamond Buff
SPI Finish A-2 — Grade #6, 3000 Grit Diamond Buff
SPI Finish A-3 — Grade #15, 1200 Grit Diamond Buff
NON-GLOSSY SURFACE, PAPER POLISH
SPI Finish B-1 — 600 Grit Paper
SPI Finish B-2 — 400 Grit Paper
SPI Finish B-3 — 320 Grit Paper
ROUGH SURFACE, STONE POLISH
SPI Finish C-1 — 600 Grit Stone
SPI Finish C-2 — 400 Grit Stone
SPI Finish C-3 — 320 Grit Stone
VERY ROUGH SURFACE, DRY BLASH POLISH
SPI Finish D-1 — 600 Stone Prior to Dry Blast Glass Bead #11
SPI Finish D-2 — 400 Stone Prior to Dry Blast #240 Oxide
SPI Finish D-3 — 320 Stone Prior to Dry Blast #24 Oxide
However, the above guideline falls short because it does not mention what steel should be used. For coarse surface, it may be fine. For demanding high glossy mold finish, the mold steel can be critical and the high glossy cannot be achieved without proper steel.
For molding process, a melt plastic resin will be injected into a steel mold at high pressure and the steel will always face the issue of wear off. To produce a glossy product, the mold has to be significantly hard so that the shiny smooth surface will not be deteriorated quickly and the glossy surface can be remained for a longer period of time. The finer the surface is needed, the harder and the finer the steel is required.
Below is a supplementary guideline regarding steel to be used.
SPI Finish A1 – S136 Hardness at 54HRC
(Generally called “Super High Glossy” in China)
SPI Finish A2 – 718HH or NAK80 Hardness at 40HRC
(Generally called “High Glossy” in China)
SPI Finish A3 – 718H or S136 Hardness 32HRC
(Generally called “Normal Glossy” in China)
It is true that the steel made in China are somehow less consistent than from overseas. Therefore, it is suggested to use imported steel for demanding quality mold or at least use higher grade of steel from China to provide some buffer for the desired mold finish that you need.
Lastly, a high glossy mold finish is not equivalent to a high glossy finished product. It is significantly subject to other factors such as plastic resin used, molding condition and mold design. For example, ABS will provide higher glossy than PP, high temperature molding condition and non-flat surface will help to provide a much glossy finished product.
Regards for all your efforts that you have put
in this. very interesting information.
best site
i love you blog
i live you site
This article is very incredible, just what i was looking for to read on my travels. Thanx
That’s right
In this case, you should expect a significant cost increase because it is very time consuming to polish deep, narrow slots in molds.
I’m very pleased to discover this page. I want to to
thank you for your time for this particularly fantastic read!!
I definitely really liked every little bit of it and i also have you saved to fav to look at new things on your
blog.
I’ve been exploring for a bit for any high-quality articles or blog posts in this kind of area .
Exploring in Yahoo I finally stumbled upon this web
site. Studying this information So i am satisfied to convey that I’ve a very good uncanny feeling I came upon exactly what I
needed. I such a lot indisputably will make certain to do not
overlook this web site and provides it a look
regularly.
Hi, I do believe this is an excellent blog. I stumbledupon it 😉 I may come back yet again since I bookmarked it.
Money and freedom is the best way to change,
may you be rich and continue to guide other people.