Mold Finish – SPI Standard and the practical approach
SPI is the short form of the Society of Plastic Industry, who establish standards for plastic industry and the SPI Plastic Engineering Handbooks is one of the most important reference for engineers.
SPI defines the polishing standard on mold finish and widely applied in US markets. It helps to avoid grey areas and measure the finest of surface in the unit of Rough Average (Ra).
Nowadays, China’s standard is very much in line with SPI. However, there is little help using Ra value in China mold making industry because there is little chance to have precise equipment at site to do the precision measurement. What we needed is a practical guideline to more or less achieve the desired mold finish. Below guideline is widely accepted.
GLOSSY SURFACE, DIAMOND BUFF POLISH
SPI Finish A-1 — Grade #3, 6000 Grit Diamond Buff
SPI Finish A-2 — Grade #6, 3000 Grit Diamond Buff
SPI Finish A-3 — Grade #15, 1200 Grit Diamond Buff
NON-GLOSSY SURFACE, PAPER POLISH
SPI Finish B-1 — 600 Grit Paper
SPI Finish B-2 — 400 Grit Paper
SPI Finish B-3 — 320 Grit Paper
ROUGH SURFACE, STONE POLISH
SPI Finish C-1 — 600 Grit Stone
SPI Finish C-2 — 400 Grit Stone
SPI Finish C-3 — 320 Grit Stone
VERY ROUGH SURFACE, DRY BLASH POLISH
SPI Finish D-1 — 600 Stone Prior to Dry Blast Glass Bead #11
SPI Finish D-2 — 400 Stone Prior to Dry Blast #240 Oxide
SPI Finish D-3 — 320 Stone Prior to Dry Blast #24 Oxide
However, the above guideline falls short because it does not mention what steel should be used. For coarse surface, it may be fine. For demanding high glossy mold finish, the mold steel can be critical and the high glossy cannot be achieved without proper steel.
For molding process, a melt plastic resin will be injected into a steel mold at high pressure and the steel will always face the issue of wear off. To produce a glossy product, the mold has to be significantly hard so that the shiny smooth surface will not be deteriorated quickly and the glossy surface can be remained for a longer period of time. The finer the surface is needed, the harder and the finer the steel is required.
Below is a supplementary guideline regarding steel to be used.
SPI Finish A1 – S136 Hardness at 54HRC
(Generally called “Super High Glossy” in China)
SPI Finish A2 – 718HH or NAK80 Hardness at 40HRC
(Generally called “High Glossy” in China)
SPI Finish A3 – 718H or S136 Hardness 32HRC
(Generally called “Normal Glossy” in China)
It is true that the steel made in China are somehow less consistent than from overseas. Therefore, it is suggested to use imported steel for demanding quality mold or at least use higher grade of steel from China to provide some buffer for the desired mold finish that you need.
Lastly, a high glossy mold finish is not equivalent to a high glossy finished product. It is significantly subject to other factors such as plastic resin used, molding condition and mold design. For example, ABS will provide higher glossy than PP, high temperature molding condition and non-flat surface will help to provide a much glossy finished product.
I was just looking for this information for a while. After 6 hours of continuous Googleing, at last I got it in your web site. I wonder what is the Google’s problem that doesn’t rank this kind of informative web sites closer to the top. Normally the top sites are full of garbage.
You could certainly see your expertise in the work you write. The sector hopes for more passionate writers such as you who aren’t afraid to say how they believe. All the time go after your heart.
You make a great point. Got some great info here. I think that if more people thought about it that way, they’d have a better time get the hang ofing the issue.
Oh my goodness! an amazing article dude. Thank you However I am experiencing issue with ur rss . Don’t know why Unable to subscribe to it. Is there anyone getting identical rss problem? Anyone who knows kindly respond. Thnkx
With havin so much content do you ever run into any problems of plagorism or copyright infringement? My blog has a lot of exclusive content I’ve either written myself or outsourced but it seems a lot of it is popping it up all over the web without my agreement. Do you know any ways to help prevent content from being ripped off? I’d genuinely appreciate it.
Keep up the excellent piece of work, I read few posts on this internet site and I conceive that your weblog is rattling interesting and has lots of good info.
I’ve been browsing online more than 3 hours today, yet I never found any interesting article like yours. It’s pretty worth enough for me. Personally, if all website owners and bloggers made good content as you did, the net will be a lot more useful than ever before.
I wish more people would take down sites like this that are actually accommodating to read. With all the balls up floating almost on the spider’s web, it is rare to be familiar with a place like yours instead.
Hi. I just pointed out that your site seems like it features a number of signal blunders at the very top of your web sites web page. Im not positive that most people are acquiring this particular common problem when surfing around your site? We are getting a completely different browser compared to a lot of people, known as Safari, to ensure is what could possibly be causing the idea? I simply wanted to be sure you know. Many thanks for putting up some terrific listings along with Not well make an effort to return back with a very different browser to test issues away!
We are a bunch of volunteers and opening a new scheme in our community. Your web site offered us with valuable information to work on. You have performed an impressive job and our entire neighborhood might be grateful to you.